Ferrite Pot Magnet with Countersink, FPC-16-Y33-Zn, POTMAGNETE

Home > Products Show > Ferrite Pot Magnets > Ferrite Pot with Countersunk > Ferrite Pot Magnet with Countersink

Ferrite Pot Magnet with Countersink

Original Image

Product Name:Ferrite Pot Magnet with Countersink
Model No:FPC-16-Y33-Zn
Specifications:
1. Powerful permanent pot magnet
2. High quality & best price
3. High working temperature
4. Good corrosion resistance
Original Manufacturer:HangSeng Magnetech
Solution:Customized your required material, size, coating, shape, grade, pull force and woking temperature
Origin:Ningbo, Zhejiang, China
Supply Ability:50000pcs/day
Certification:SGS,TUV,ISO9001,ROHS,TS16949
Applications:magnetic holding, lifting, antenna Mounting, positioning, retrieving and much more.

Detailed Product Description:

Magnet Shape: Ring with Countersunk (Countersink)
Material: Hard Ferrite (Ceramic) and Steel
Coating: Zinc(Zn) / Nickel(Ni)
Grade(Chinese Stardard):         Y33
Magnet ID:              FPC-16-Y33-Zn
Detailed magnetic properties data:
Residual Magnetic Flux Density (Br): 4.1-4.3 KGs (mT): 410-430 mT
Intrinsic Coercivity Force (Hcj):    2.76-3.14 KOe    220-250 KA/m
Coercivity Force (Hcb):              2.83-3.20 KOe    225-255 KA/m
Energy Density (BH)max:              3.9-4.4 MGOe     31.5-35.0 KJ/mÂ³
Operating Temperature:               -40 Â°C to +250 Â°C
Magnetisation Direction: Axial / Radially magnetized
Pot Magnet Size:
Pot Total height (H):       4.5 mm
Pot Total diameter (D):     16 mm
Pot Diameter top (d2):      3.5 mm
Pot Diameter bottom (d3):   6.5 mm
Countersunk depth (h3):     1.7 mm
Tolerance:         +/-2% mm
Delivery time           7-25 days
Measurements

Ferrite Magnets
Our company has been widely acclaimed for providing our clients with this extensive range of Ferrite Magnets that has been extensively composed of best quality iron and barium or strontium oxides. The offered magnet is hard in composition and can be easily categorized by high normal & intrinsic coercive force. In addition to this a rather low residual induction and are virtually free from the effects of a self-demagnetization. Offering a corrosion free ferrite, it is also used for treatments as it posses a comparatively high electric resistivity.